原包美國SABIC增強無鹵防火PC Lexan 3412ECR-131
Density / Specific Gravity | |||
-- | 1.30 | g/cm3 | ASTM D792 |
-- | 1.36 | g/cm3 | ISO 1183 |
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 7.0 | g/10 min | ASTM D1238 |
Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 7.0 | cm3/10min | ISO 1133 |
Molding Shrinkage | Internal Method | ||
Across Flow : 3.20 mm | 0.20 to 0.50 | % | |
Flow : 3.20 mm | 0.20 to 0.50 | % | |
Water Absorption | ISO 62 | ||
Saturation, 23°C | 0.29 | % | |
Equilibrium, 23°C, 50% RH | 0.12 | % |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | |||
-- 2 | 5500 | MPa | ASTM D638 |
-- | 6000 | MPa | ISO 527-2/1 |
Tensile Strength | |||
Yield 3 | 90.0 | MPa | ASTM D638 |
Yield | 95.0 | MPa | ISO 527-2/5 |
Break 3 | 87.0 | MPa | ASTM D638 |
Break | 90.0 | MPa | ISO 527-2/5 |
Tensile Elongation | |||
Yield 3 | 3.1 | % | ASTM D638 |
Yield | 2.8 | % | ISO 527-2/5 |
Break | 3.2 | % | ISO 527-2/5 |
Flexural Modulus | |||
50.0 mm Span 4 | 5000 | MPa | ASTM D790 |
-- 5 | 5500 | MPa | ISO 178 |
Flexural Stress | |||
-- 5, 6 | 140 | MPa | ISO 178 |
Yield, 50.0 mm Span 4 | 156 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength 7 | ISO 179/1eA | ||
-30°C | 5.0 | kJ/m2 | |
23°C | 6.0 | kJ/m2 |
原包美國SABIC增強無鹵防火PC Lexan 3412ECR-131